Kinetic analysis of formation of magnesia spinel by thermal analysis

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

Thermal analysis of mixtures ofvarious alumina precursors (powders of fused corundum, smelter-grade alumina GKand non-smelter-grade alumina G-00, combustion product of xerogel from aluminumnitrate and citric acid) with periclase at different heating ratesis performed. By analyzing the shape and position of exothermicpeaks, which corresponded to the formation of magnesia spinel MgAl2O4, the values of the Avrami coefficient and theeffective values of the activation energy are determined according toKissinger, Augis-Bennett, and Ozawa equations. The effect of mechanoactivation (MA)of the reactants is analyzed. Co-treatment of periclase and corundum-containingreagents allowed reducing the activation energy of the reaction by15–20%. Pre-treatment of one of the components of the mixtureis most appropriate for periclase since it allowed reducingЕаby ~14%, whereas MA of corundum alone reduced thischaracteristic only by ~9%. Using the combustion product ofxerogel of alumina-oxide composition in spinel synthesis is very effectivesince it accelerated the process by reducingЕаby~11% even without MA. The values of the Avrami constantare found to be in the range 0.57–0.76, which correspondsto the mechanism of nucleation and crystal growth.

作者简介

N. Filatova

Ivanovo State University of Chemistry and Technology

Email: zyanata@mail.ru
Ivanovo, Russia

N. Kosenko

Ivanovo State University of Chemistry and Technology

Email: zyanata@mail.ru
Ivanovo, Russia

A. Artyushin

Ivanovo State University of Chemistry and Technology

编辑信件的主要联系方式.
Email: zyanata@mail.ru
Ivanovo, Russia

参考

  1. Obradović N., Filipović S., Fahrenholtz W.G., et al. // Scienceof Sintering. 2023. V. 55. № 1. P. 1. https://doi.org/10.2298/SOS2301001O
  2. Chen Z., Yan W., L G.i, et al. //J.of the European Ceramic Society. 2024. V. 44.Is. 2. P. 1070. https://doi.org/10.1016/j.jeurceramsoc.2023.10.004
  3. Gajdowski C., D’Elia R., FaderlN., et al. // Ceram. Int.2022. V. 48. P. 18199. doi: 10.1016/j.ceramint.2022.03.079
  4. Baruah B., Bhattacharyya S., Sarkar R. // AppliedCeramic Technology. 2023. V. 20. Is. 3. P. 1331. https://doi.org/10.1111/ijac.14309
  5. Zegadi A., Kolli M., Hamidouche M., Fantozzi G. //Ceramics International. 2018. V. 44. P. 18828. https://doi.org/10.1016/j.ceramint.2018.07.117
  6. Косенко Н.Ф. Смирнова М.А. // Огнеупорыи техническая керамика. 2011. № 9. С. 3.
  7. Tran A., Tran V., Nguyet N.T.M.,et al. // ACS Omega.2023. V. 8. P. 36253. https://doi.org/10.1021/acsomega.3c04782
  8. Liu J., Lv X., Li J., et al. //Science of Sintering. 2016. V. 48. P. 353. http://dx.doi.org/10.2298/SOS1603353L
  9. Obradović N., Fahrenholtz W.G.,Filipović S., et al. // J. of Thermal Analysis and Calorimetry. 2020. V. 140.P. 95. https://doi.org/10.1007/s10973-019-08846-w
  10. Филатова Н.В., Косенко Н.Ф., Артюшин А.С.и др. // Росс. хим. журн. 2024. Т. 68. № 2.
  11. Filatova N.V., Kosenko N.F., Denisova O.P. // Russ. J. of PhysicalChemistry A. 2022. V. 96. № 6. P. 1147. http://dx.doi.org/10.1134/S0036024422060085
  12. Gotor F.J., Criado J.M., Malek J., Koga N. // J. Phys. Chem. A.2000. V. 104. Is. 46.P. 10777. https://doi.org/10.1021/jp0022205
  13. Sinhamahapatra S.,Shamim M., Tripathi H.S.,et al. // Ceramics International. 2016. V. 42. P. 9204. http://dx.doi.org/10.1016/j.ceramint.2016.03.017
  14. Filatova N.V., Kosenko N.F., Badanov M.A. //ChemChemTech [Izv. Vyssh. Uchebn. Zaved. Khim. Khim. Tekhnol.]. 2021.V. 64. № 11. P. 97. https://doi.org/10.6060/ivkkt.20216411.6478
  15. Han Y.,Li H. // Case Studies in Thermal Engineering. 2023. V.45. Art. 102993. https://doi.org/10.1016/j.csite.2023.102993
  16. Kissinger H.E. // J. Res.Natl. Bur. Stand. 1956. V. 56. P. 217.
  17. Augis J.A.,Bennett J.E. // J. Therm. Anal. 1978. V. 13. P. 283.
  18. Ozawa T. // Bull. Chem. Soc. Jpn. 1965.V. 35. P. 1881.
  19. Watson E.B., Price J.D. // Geochim. Cosmochim. Acta. 2002 V. 66. Is. 12.P. 2123. https://doi.org/10.1016/S0016-7037(02)00827-X

补充文件

附件文件
动作
1. JATS XML
下载

版权所有 © Russian Academy of Sciences, 2025